Product Details:
Payment & Shipping Terms:
|
| Boron Carbide Bulletproof Plate: | NIJ IV Boron Carbide Ballistic Ceramic Tile | Silicon Carbide Bulletproof Plate: | NIJ IV Silicon Carbide Ballistic Ceramic Tile |
|---|---|---|---|
| NIJ III Bullet Proof Panel Ballistic Plate: | NIJ III Lightweight High Level Bullet Proof Panel Ballistic Plate Single-curve Pure Armored UHMWPE Plate | Bulletproof Plate By Boron Carbide Material: | B4C Bulletproof Ceramic Ballistic Plate And Tile |
| Density: | 2.5 G/cm3 | Grade: | NIJ III, NIJ IV Ballistic Ceramic Tile |
| Hardness: | 30.83Gpa, Vickers | Sic Ballistic Tiles: | Silicon Carbide Armor Tiles For Ballistic Protection |
| Highlight: | ballistic ceramic tile,Ballistic Armour Plates |
||
Alumina Silicon Carbide ballistic tile / Boron carbide Ceramic Tile Typical for Bullet Proof Plate
• made of boron carbide ,silicon carbide or Alumina
• lightweight,high toughness
• for aircraft armor,vehicle armor
• for body armor
Description:
Boron carbide bulletproof armor plate is made by sintereting boron carbide abrasive grain in the
high pressure vacuum sintering furnace, from room temperature to a certain temperature, keep this temperature for several hours then naturally cooling to room temperature again, then processing it mechanically to reach a required tolerance.
Applications:
Ceramic bulletproof armor plate is suitable for making lightweight bulletproof armor, using to protect aircraft, vehicle, naval vessel and making bullet-proof vest.
Typical Chemical Analysis:
Total Boron 77.90%
Total Carbon 20.98%
Fe2O3 0.16%
B+C 98.88%
B4C 95.85%
Physical Properties:
Color Grey
Bending Strength 469Mpa
Fracture Toughness 4.2Mpa.m1/2
Density 2.56 g/cm3
Hardness 30.83Gpa, Vickers
Dimension Available :
| Length(mm) | Width(mm) | Thickness(mm) |
| 50 | 50 | 8-10 |
| 150 | 150 | 5-10 |
| 200 | 200 | 5-10 |
Hexagon, single spherical side, double spherical side, arc shape and OEM dimension available upon request.
Material Comparation Chart:
| Item | Al2O3 | SiC | B4C |
| Density | 3.5g/cm3 | 3.1g/cm3 | 2.4-2.65g/cm3 |
| Hardness | HV1650 | HV2750 | HV3300 |
| Flexural strength | 290 Mpa | 380 Mpa | 400-650 Mpa |
| Compressive strength | 850 Mpa | 3970 Mpa | 4100 Mpa |
| Fracture toughness | 4.8 Mpa.m1/2 | 4.0 Mpa.m1/2 | 4.5-7.0 Mpa.m1/2 |
| Thermal Conductivity | 20 m0k | 120m0k |
29 m0k |
Workshop & Warehouse & Lab: